Copper Putty

about us

Repair of Copper parts/castings

A two component paste, based on a copper powder filled epoxy system. The non-rusting, non magnetic dependable inert putty extensively used for fairing, repair, filling or patching of copper castings and equipment where copper finish is desired.

Best Buying Price- VISIT

USDollerOut Side of India

IndianRupeeWithin India

 

Appliaction Tools

Free

Private Label

private-label

Features of Copper Putty

  • Fast,cost effective and durable
  • High compressive strength and extreme chemical resistance Good resistance to abrasion, friction reduction and hence ideal for turn-around time.
  • The product may be applied to any unlimited thickness onto horizontal or vertical surfaces
  • Efficient alternate method of repair where welding or brazing would be undesirable or impossible
  • Can Repair Intricate shape or forms/thin sections, difficult to weld metals
  • No equipment/Power supply needed
  • Unlimited cycle of repairs
  • Less Labor costs - Avoid assembly/disassembly, Pre Machining/Post Machining Resistant to chemicals and most acids, bases, solvents, and alkalis.
  • It can be easily Can be machined, drilled, tapped or painted
  • Superior adhesion – forms a solid bond to steel, cast iron,
  • Stainless steel, concrete, and clean and abraded bronze, copper, and aluminum.
  • Eliminates costly wear part inventory
  • No shrinkage, expansion or distortion
  • Excellent electrical insulation characteristics
  • Can do repairs at In-situ repair, In-Plant, Workshops, Remote areas
  • No VOC’s
  • Routine Maintenance and Unexpected Maintenance
  • Repair cost at fraction of replacement cost

Appliaction Demo

unit
unit

Where to Use?

  • Copper/Brass Parts & Equipments
Product Specification Details
PROPERTIES STANDARD UNIT VALUES
Pack Size gms 500
COVERAGE @ 5mm thickness - cm2/pack size/thickness 597Cm2 / kg / 5 mm
Color and Apperance ASTM D 1544 - Copper & Thick paste
Specific Gravity ASTM D 1475-98 - 2.1
Mix Ratio By Weight Manual - 4(R):1(H)
Mix Ratio By Volume Manual - 4(R):1(H)
Pot Life @ 30°C IS 101 min 50
Functional Cure ASTM D 1640 Hrs 24
Compressive Strength ASTMD 695 N/mm2 58.05
Adhesive Shear Strength ASTM D1002 N/mm2 18.2